Repair material KS-2

General Information

The product is composed of raw materials such as corundum, super grade bauxite and mullite, adding electromolten chromium oxide green to improve the corrosion resistance of the material. The main applications are: intermediate frequency furnace lining repair, ladle/iron ladle/non-ferrous metal ladle, steel and non-ferrous metal all contact parts, easy to use, users can use directly on site; At the same time, it has the characteristics of no mold, and can enter the baking stage directly without maintenance after construction. After baking, it has the characteristics of high strength, strong thermal impact resistance, excellent thermal insulation performance and strong corrosion and penetration resistance.

Physical and chemical indicators (Technical Data)

Standard Packaging and Storage

Packing in 25kg plastic drum or carton; Store in a cool place at room temperature, avoid opening the bag in the exposed air, or store in a place of exposure and high temperature.

Construction Technology (Conatruction Technology)

Please refer to the company's "High Performance repair material construction technical operating rules"

High performance repair material construction technical operating rules

I. Construction

    High performance repair material is a kind of corundum, super bauxite and mullite composed of plastic, the use of ramming compaction molding method for molding construction, the construction of the first manual plastic according to the required thickness laid in the required parts, and then with a hammer or a hand hammer ramming strong, the construction site is narrow, can be rammed with long wood, generally not too heavy, The construction surface can not be rammed to the surface like refractory concrete to produce grout, otherwise it is not conducive to the density and moisture volatilization of the internal structure of the plastic, so the construction surface is not easy to wipe and smooth. When ramming thicker, you can needle a little porosity, hole depth can be 1/2 of the thickness of the plastic, and the interval between the holes is 100mm, which is convenient for baking and removing water.

Second, baking

The oven is an important link, but the plastic water content is more, the baking temperature should be strictly controlled, especially in the low temperature state, the temperature must be slow, such as heating too fast, a large amount of water from the plastic too fast discharge, can cause plastic expansion, cracks, peeling and other adverse phenomena, affecting the use of effect.

The specific operation temperature rise is as follows:

Note: 1. Baking time from 0 to about 27h end;

2. Temperature rise is uniform temperature rise, in the real situation, as far as possible to achieve more uniform temperature rise; ,

3. The flame length is estimated according to experience, and the operation is handled according to the actual situation on site

         4. When the fire is baking, the high temperature is about 1000℃, which can be slightly increased and should not be lower than 1000℃.

5. The specific baking scheme can be adjusted according to the site situation.